| 熔指(MFR) | 300℃/1.2Kg | 7 | g/10min | ASTM D1238 |
| 密度 | 1200 | kg/m³ | ASTM D792 | |
| 收缩率 | 0.005-0.007 | % | ASTM D955 | |
| 吸水率 | 23℃,24hr | 0.15 | % | ASTM D570 |
| 吸水率 | 23℃,50RH,24hr平衡 | 0.32 | % | ASTM D570 |
| 拉伸模量 | 2410 | MPa | ASTM D638 | |
| 拉伸屈服强度 | 60 | MPa | ASTM D638 | |
| 拉伸强度 | 72 | MPa | ASTM D638 | |
| 屈服伸长率 | 6 | % | ASTM D638 | |
| 断裂伸长率 | 150 | % | ASTM D638 | |
| 弯曲强度 | 96 | MPa | ASTM D790 | |
| 弯曲模量 | 2410 | MPa | ASTM D790 | |
| 悬臂梁缺口冲击强度 | 23℃ | 900 | J/m | ASTM D256 |
| 洛氏硬度 | M | 74 | 无 | ASTM D785 |
| 热变形温度 | 0.45MPa退火 | 145 | °C | ASTM D648 |
| 热变形温度 | 1.8MPa退火 | 142 | °C | ASTM D648 |
| 热变形温度 | 1.8MPa未退火 | 129 | °C | ASTM D648 |
| 维卡软化点 | 50℃/hr,50N | 151 | °C | ASTM D1525 |
| 线性膨胀系数 | -40-82℃ | 6.8E-5 | °C | ASTM D696 |
| 球压试验 | 125 | 无 | IEC 60695 | |
| 体积电阻率 | 23℃,干燥 | 2E+17 | ohms·cm | ASTM D257 |
| 介电强度 | 17 | kV/mm | ASTM D149 | |
| 介电常数 | 60Hz | 3 | 无 | ASTM D150 |
| 耗散因数 | 60Hz | 0.001 | 无 | ASTM D150 |
| 漏电起痕指数 | 2mm | 250 | V | IEC 60112 |
| 阻燃等级 | 1.5mm | HB | 无 | UL 94 |
| 阻燃等级 | 3.0mm | HB | 无 | UL 94 |
| 灼热丝起燃温度 | 2mm | 850 | °C | IEC 60695 |
| 极限氧指数 | 26 | % | ASTM D2863 | |
| 黄度指数 | -0.04 | 无 | ASTM E313 |