总体描述
材料状态
流通正常
认证
已认证
特性
用途
加工方法
形态
粒子
| 熔指(MFR) | 300℃/1.2kg | 5 | g/10min | ASTM D1238 |
| 收缩率 | MD | 0.5-0.7 | % | ASTM D955 |
| 密度 | 1.2 | g/cm³ | ASTM D792 | |
| 收缩率 | MD | 0.5-0.7 | % | ASTM D955 |
| 吸水率 | 平衡，23℃，50% RH | 0.32 | % | ASTM D570 |
| 吸水率 | 23℃，24hr | 0.15 | % | ASTM D570 |
| 悬臂梁缺口冲击强度 | 23℃，3.2mm | 950 | J/m | ASTM D256 |
| 落镖冲击 | 23℃，3.2mm | 94 | J | ASTM D3763 |
| 拉伸模量 | 2480 | MPa | ASTM D638 | |
| 拉伸断裂强度 | 42 | MPa | ASTM D638 | |
| 拉伸屈服强度 | 60 | MPa | ASTM D638 | |
| 断裂伸长率 | 150 | % | ASTM D638 | |
| 屈服伸长率 | 6 | % | ASTM D638 | |
| 弯曲模量 | 2410 | MPa | ASTM D790 | |
| 弯曲强度 | 96 | MPa | ASTM D790 | |
| 洛氏硬度 | M | 74 | 无 | ASTM D785 |
| 洛氏硬度 | R | 11B | 无 | ASTM D785 |
| 热变形温度 | 1.8MPa，退火 | 143 | ℃ | ASTM D648 |
| 热变形温度 | 1.8MPa，未退火 | 132 | ℃ | ASTM D648 |
| 热变形温度 | 0.45MPa，退火 | 146 | ℃ | ASTM D648 |
| 维卡软化点 | 151 | °C | ASTM D1525 5 | |
| 线性膨胀系数 | MD，-40 - 82℃ | 6.8E-5 | °C | ASTM D696 |
| 体积电阻率 | 23℃ | 2E+7 | ohms·cm | ASTM D257 |
| 介电强度 | 17 | kV/mm | ASTM D149 | |
| 介电常数 | 60 Hz | 3 | 无 | ASTM D150 |
| 耗散因数 | 60 Hz | 1E-3 | 无 | ASTM D150 |
| 相对漏电起痕指数 | 2mm | 250 | V | IEC 60112 |
| 阻燃等级 | 0.5mm | V2 | 无 | UL 94 |
| 阻燃等级 | 1.6mm | V2 | 无 | UL 94 |
| 阻燃等级 | 2.5mm | V2 | 无 | UL 94 |
| 阻燃等级 | 3.0mm | V2 | 无 | UL 94 |
| 灼热丝起燃温度 | 2mm | 850 | °C | IEC 60695-2-13 |
| 极限氧指数 | 26 | % | ASTM D2863 |